Standard Test Method for Notch Tensile Test to Measure the Resistance to Slow Crack Growth of Polyethylene Pipes and Resins

$83.00

$83.00

$149.40


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


...

1.1 This test method determines the resistance of polyethylene materials to slow crack growth under conditions specified within.

Note 1This test method is known as PENT (Pennsylvania Notch Test) test.

1.2 The test is generally performed at 80°C and at 2.4 MPa, but may also be done at temperatures below 80°C and with other stresses low enough to preclude ductile failure and thereby eventually induce brittle type of failure. Generally, polyethylenes will ultimately fail in a brittle manner by slow crack growth at 80°C if the stress is below 2.4 MPa.

1.3 The test method is for specimens cut from compression molded plaques.2 See Appendix X1 for information relating to specimens from pipe.

1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.


5.1 This test method is useful to measure the slow crack growth resistance of molded plaques of polyethylene materials at accelerated conditions such as 80°C, 2.4-MPa stress, and with a sharp notch.

5.2 The testing time or time to failure depends on the following test parameters: temperature; stress; notch depth; and specimen geometry. Increasing temperature, stress, and notch depth decrease the time to failure. Thus, in reporting the test time or time to failure, all the conditions of the test shall be specified.

SDO ASTM: ASTM International
Document Number F1473
Publication Date Aug. 1, 2013
Language en - English
Page Count 7
Revision Level 13
Supercedes
Committee F17.40
Publish Date Document Id Type View
Sept. 1, 2024 F1473-24A Revision
April 1, 2024 F1473-24 Revision
July 1, 2023 F1473-23 Revision
Feb. 1, 2018 F1473-18 Revision
Aug. 15, 2016 F1473-16 Revision
Aug. 1, 2013 F1473-13 Revision
May 1, 2011 F1473-11 Revision
May 1, 2007 F1473-07 Revision
May 10, 2001 F1473-97E01 Revision
May 10, 2001 F1473-01E01 Revision
May 10, 2001 F1473-01 Revision