ASTM F1472-23

Current Revision

Standard Specification for Wrought Titanium-6Aluminum-4Vanadium Alloy for Surgical Implant Applications (UNS R56400)

$69.00

$69.00

$124.20

$83.00

$83.00

$149.40



Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

...

1.1 This specification covers the chemical, mechanical, and metallurgical requirements for wrought annealed titanium-6aluminum-4vanadium alloy (UNS R56400) to be used in the manufacture of surgical implants.

1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.

1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.


This specification covers the requirements for wrought titanium-6aluminum-4vanadium alloy for use in surgical implant applications. The material shall be manufactured by multiple melting in plasma arc and electron beam furnaces into strip, sheet, plate, bar, forging bar, or wire. The material shall be available in the annealed or cold-worked condition, with the surface mechanically descaled or pickled, sandblasted, chemically milled, ground, machined, peeled, polished, or a combination of these. Heat and product analyses as well as tension and bend (for sheet, strip, and plate) tests shall be performed and shall conform to the requirements specified. In addition, the material shall have a microstructure consisting of a fine dispersion of alpha and beta phases as a result of processing in the alpha plus beta field, with no continuous alpha network at prior beta grain boundaries and no coarse, elongated alpha platelets.


SDO ASTM: ASTM International
Document Number F1472
Publication Date Feb. 1, 2023
Language en - English
Page Count 6
Revision Level 23
Supercedes
Committee F04.12
Publish Date Document Id Type View
Feb. 1, 2023 F1472-23 Revision
Nov. 1, 2020 F1472-20A Revision
Aug. 1, 2020 F1472-20 Revision
Nov. 15, 2014 F1472-14 Revision
Oct. 1, 2008 F1472-08E01 Revision
Oct. 1, 2008 F1472-08 Revision
Nov. 10, 2002 F1472-02A Revision
April 10, 2002 F1472-02 Revision
Nov. 10, 2000 F1472-99 Revision
Nov. 10, 2000 F1472-00 Revision