1.1 This specification2 covers rod of low-carbon nickel-chromium-molybdenum alloys (UNS N10276, N06022, N06035, N06044, N06455, N06058, and N06059), low-carbon nickel-molybdenum-chromium (USN N10362), low-carbon nickel-molybdenum-chromium-tantalum (UNS N06210), low-carbon nickel-chromium-molybdenum-copper alloy (UNS N06200), and low-carbon nickel-chromium-molybdenum-tungsten (UNS N06686) as shown in Table 1, for use in general corrosive service.

1.2 The following products are covered under this specification:

1.2.1 Rods 5/16 to 3/4 in. (7.94 to 19.05 mm), exclusive, in diameter, hot or cold finished, solution annealed and pickled, or mechanically descaled.

1.2.2 Rods 3/4 to 31/2 in. (19.05 to 88.9 mm), inclusive, in diameter, hot or cold finished, solution annealed, ground or turned.

1.2.3 Rods 1/4 to 3 1/2 in. (6.35 to 88.9 mm), inclusive, in diameter, solution annealed, cold finished, as cold finished, ground or turned (N06059 and N06686 only, see Table 2 and Table 3).

1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.

1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.


This specification2 covers rod of low-carbon nickel-chromium- molybdenum alloys (UNS N10276, N06022, N06035, N06455, N06058, and N06059), low-carbon nickel-molybdenum- chromium-tantalum (UNS N06210), low-carbon nickel-chromium-molybdenum-copper alloy (UNS N06200), and low-carbon nickel-chromium-molybdenum-tungsten (UNS N06686), for use in general corrosive service. Product and chemical analyses shall be performed on the materials and shall conform to the required chemical composition in molybdenum, chromium, iron, tungsten, cobalt, carbon, silicon, manganese, vanadium, phosphorus, sulfur, titanium, nickel, aluminum, copper, and tantalum. Tension test shall be performed and shall comply to required mechanical properties for hot or cold finished, solution annealed rods such as tensile strength, yield strength, and elongation.


SDO ASTM: ASTM International
Document Number B574
Publication Date Nov. 1, 2018
Language en - English
Page Count 6
Revision Level 18
Supercedes
Committee B02.07
Publish Date Document Id Type View
Nov. 1, 2023 B0574-23 Revision
Nov. 1, 2018 B0574-18 Revision
June 1, 2017 B0574-17 Revision
Oct. 1, 2015 B0574-15 Revision
Oct. 1, 2010 B0574-10 Revision
June 1, 2006 B0574-06E01 Revision
June 1, 2006 B0574-06 Revision
Feb. 1, 2005 B0574-05 Revision
Feb. 1, 2004 B0574-04 Revision
Oct. 10, 1999 B0574-99A Revision