1.1 This specification establishes the requirements for high conductivity, tough-pitch, copper wire bars, cakes, slabs, billets, ingots, and ingot bars.
1.2 Copper under this specification corresponds to the designations “ETP” (UNS C11000) and “FRHC” (UNS C11020) as shown in Classification B224. These coppers may also be used to produce coppers corresponding to the following:
Copper UNS No. | Classification B224 Designation |
| |
C11300, C11400, C11500, and C11600 | STP |
C12000 | DLP |
C12200 | DHP |
C12300 | DHPS |
C14520 | DPTE |
1.3 Although this specification includes certain UNS designations as described in Practice E527, these designations are for cross reference only and are not specification requirements. Therefore, in case of conflict, this ASTM specification shall govern.
1.4 Units—The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.4.1 Exception—Electrical resistivity is expressed in SI units.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
This specification establishes the requirements for high conductivity, tough-pitch, copper wire bars, cakes, slabs, billets, ingots, and ingot bars. Copper wires under this specification include UNS C113000, C11400, C11500 and C11600, C12000, C12200, C12300, and C14500. The maximum values of mass resistivity for wire bars, cakes, slabs, and billets, for electrical use and for other uses, shall conform to the specified requirements. Samples for the electrical resistivity test of electrolytic copper, electrorefined copper, electrowon copper, and fire-refined copper shall be fabricated into a rod. The external oxide shall be removed, the rod cold drawn into a wire of a specific diameter, and cut into sampling lengths. The resulting specimen shall be annealed and quickly cooled in an inert atmosphere. The mean resistivity shall be determined as the mean of the observations from the test on the wires.
14.1 Calculated values shall be rounded to the specified number of places in accordance with Practice E29.
SDO | ASTM: ASTM International |
Document Number | B5 |
Publication Date | Oct. 1, 2022 |
Language | en - English |
Page Count | 5 |
Revision Level | 22 |
Supercedes | |
Committee | B05.07 |