ASTM B265-13

Historical Revision

Standard Specification for Titanium and Titanium Alloy Strip, Sheet, and Plate

$83.00

$83.00

$149.40

$0.00

$0.00

$0.00

Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00

Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

...

1.1 This specification2 covers annealed titanium and titanium alloy strip, sheet, and plate as follows:

1.1.1 Grade 1—Unalloyed titanium,

1.1.2 Grade 2—Unalloyed titanium,

1.1.2.1 Grade 2H—Unalloyed titanium (Grade 2 with 58 ksi minimum UTS),

1.1.3 Grade 3—Unalloyed titanium,

1.1.4 Grade 4—Unalloyed titanium,

1.1.5 Grade 5—Titanium alloy (6 % aluminum, 4 % vanadium),

1.1.6 Grade 6—Titanium alloy (5 % aluminum, 2.5 % tin),

1.1.7 Grade 7—Unalloyed titanium plus 0.12 to 0.25 % palladium,

1.1.7.1 Grade 7H—Unalloyed titanium plus 0.12 to 0.25 % palladium (Grade 7 with 58 ksi minimum UTS),

1.1.8 Grade 9—Titanium alloy (3.0 % aluminum, 2.5 % vanadium),

1.1.9 Grade 11—Unalloyed titanium plus 0.12 to 0.25 % palladium,

1.1.10 Grade 12—Titanium alloy (0.3 % molybdenum, 0.8 % nickel),

1.1.11 Grade 13—Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.12 Grade 14—Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.13 Grade 15—Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.14 Grade 16—Unalloyed titanium plus 0.04 to 0.08 % palladium,

1.1.14.1 Grade 16H—Unalloyed titanium plus 0.04 to 0.08 % palladium (Grade 16 with 58 ksi minimum UTS),

1.1.15 Grade 17—Unalloyed titanium plus 0.04 to 0.08 % palladium,

1.1.16 Grade 18—Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.04 to 0.08 % palladium,

1.1.17 Grade 19—Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum),

1.1.18 Grade 20—Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum) plus 0.04 % to 0.08 % palladium,

1.1.19 Grade 21—Titanium alloy (15 % molybdenum, 3 % aluminum, 2.7 % niobium, 0.25 % silicon),

1.1.20 Grade 23—Titanium alloy (6 % aluminum, 4 % vanadium with extra low interstitial elements, ELI),

1.1.21 Grade 24—Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.04 % to 0.08 % palladium,

1.1.22 Grade 25—Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.3 % to 0.8 % nickel and 0.04 % to 0.08 % palladium,

1.1.23 Grade 26—Unalloyed titanium plus 0.08 to 0.14 % ruthenium,

1.1.23.1 Grade 26H—Unalloyed titanium plus 0.08 to 0.14 % ruthenium (Grade 26 with 58 ksi minimum UTS),

1.1.24 Grade 27—Unalloyed titanium plus 0.08 to 0.14 % ruthenium,

1.1.25 Grade 28—Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.08 to 0.14 % ruthenium,

1.1.26 Grade 29—Titanium alloy (6 % aluminum, 4 % vanadium with extra low interstitial elements, ELI) plus 0.08 to 0.14 % ruthenium,

1.1.27 Grade 30—Titanium alloy (0.3 % cobalt, 0.05 % palladium),

1.1.28 Grade 31—Titanium alloy (0.3 % cobalt, 0.05 % palladium),

1.1.29 Grade 32—Titanium alloy (5 % aluminum, 1 % tin, 1 % zirconium, 1 % vanadium, 0.8 % molybdenum),

1.1.30 Grade 33—Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.02 5 % ruthenium, 0.15 % chromium),

1.1.31 Grade 34—Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),

1.1.32 Grade 35—Titanium alloy (4.5 % aluminum, 2 % molybdenum, 1.6 % vanadium, 0.5 % iron, 0.3 % silicon),

1.1.33 Grade 36—Titanium alloy (45 % niobium),

1.1.34 Grade 37—Titanium alloy (1.5 % aluminum),

1.1.35 Grade 38—Titanium alloy (4 % aluminum, 2.5 % vanadium, 1.5 % iron), and

1.1.36 Grade 39—Titanium alloy (0.25 % iron, 0.4 % silicon).

Note 1—H grade material is identical to the corresponding numeric grade (that is, Grade 2H = Grade 2) except for the higher guaranteed minimum UTS, and may always be certified as meeting the requirements of its corresponding numeric grade. Grades 2H, 7H, 16H, and 26H are intended primarily for pressure vessel use.

The H grades were added in response to a user association request based on its study of over 5200 commercial Grade 2, 7, 16, and 26 test reports, where over 99 % met the 58 ksi minimum UTS.

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.


This specification covers annealed titanium and titanium alloy strip, sheet, and plate. The grades of titanium and titanium alloy metal covered by this specification shall have the chemical composition requirements of: nitrogen, carbon, hydrogen, iron, oxygen, aluminum, vanadium, tin, ruthenium, palladium, cobalt, molybdenum, chromium, nickel, niobium, zirconium, silicon, and titanium. For sheet and strip, the bend test specimen shall stand being bent cold through without fracture in the outside of the bent portion. Product analysis tolerances cover variations between laboratories in the measurement of chemical content of the specimen. In cutting samples for analysis, the operation should be carried out insofar as possible in a dust-free atmosphere because utmost care must be used in sampling titanium for chemical analysis due to its great affinity for elements such as oxygen, nitrogen, and hydrogen. The chemical analysis shall be conducted by the standard techniques normally utilized by the manufacturer and purchaser.
SDO ASTM: ASTM International
Document Number B265
Publication Date June 1, 2013
Language en - English
Page Count 9
Revision Level 13
Supercedes
Committee B10.01
Publish Date Document Id Type View
April 1, 2020 B0265-20A Revision
Jan. 1, 2020 B0265-20 Revision
Nov. 1, 2015 B0265-15 Revision
July 1, 2013 B0265-13AE01 Revision
July 1, 2013 B0265-13A Revision
June 1, 2013 B0265-13 Revision
Sept. 1, 2011 B0265-11E01 Revision
Sept. 1, 2011 B0265-11 Revision
May 1, 2010 B0265-10 Revision
May 1, 2009 B0265-09AE01 Revision
May 1, 2009 B0265-09A Revision
April 15, 2009 B0265-09 Revision
Nov. 1, 2008 B0265-08B Revision
Aug. 1, 2008 B0265-08A Revision
May 15, 2008 B0265-08 Revision
Nov. 1, 2007 B0265-07 Revision
Dec. 1, 2006 B0265-06B Revision
June 1, 2006 B0265-06A Revision
April 1, 2006 B0265-06 Revision
Jan. 1, 2005 B0265-05E01 Revision
Jan. 1, 2005 B0265-05 Revision
Nov. 1, 2003 B0265-03 Revision
Oct. 10, 2002 B0265-02 Revision
May 10, 1999 B0265-99E01 Revision
May 10, 1999 B0265-99 Revision