Standard Specification for Nickel Rod and Bar

$83.00

$83.00

$149.40


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

...

1.1 This specification covers nickel (UNS N02200)*, low carbon nickel (UNS N02201)*, and solution strengthened nickel (UNS N02211) in the form of hot-worked and cold-worked rod and bar in the conditions shown in Table 1.

1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.

TABLE 1 Mechanical Properties

Condition and Diameter or Distance
Between Parallel Surfaces, in. (mm)
Tensile Strength, min,
psi (MPa)
Yield Strength (0.2 % offset),
min. psi (MPa)A
Elongation in 2 in. or 50 mm or 4D, min %
Nickel (UNS N02200)
Cold-worked (as worked):
Rounds, 1 (25.4) and under 80 000 (550) 60 000 (415) 10B
Rounds over 1 to 4 (25.4 to 101.6) incl. 75 000 (515) 50 000 (345)15
Squares, hexagons, and rectangles, all sizes 65 000 (450) 40 000 (275) 25B
Hot-worked:
All sections, all sizes 60 000 (415) 15 000 (105) 35C
Rings and disksD
Annealed:
Rods and bars, all sizes 55 000 (380) 15 000 (105) 40B
Rings and disksE
Forging quality
All sizes F FF
Low-Carbon Nickel (UNS N02201) and Solution Strengthened Nickel (UNS N02211)
Hot-worked:
All sections, all sizes 50 000 (345) 10 000 (70) 40C
Annealed:
All products, all sizes 50 000 (345) 10 000 (70) 40B

A See 12.2.

B Not applicable to diameters or cross sections under 3/32 in. (2.4 mm).

C For hot-worked flats 5/16 in. (7.9 mm) and under in thickness the elongation shall be 25%, min.

D Hardness B45 to B80, or equivalent.

E Hardness B45 to B70 or equivalent.

F Forging quality is furnished to chemical requirements and surface inspection only. No tensile properties are required.


This specification covers nickel (UNS N02200), low carbon nickel (UNS N02201), and solution strengthened nickel (UNS N02211) in the form of hot-worked, cold-worked, or annealed rods and bars of round, square, hexagonal, or rectangular solid section. The material shall conform to the chemical composition limits specified for nickel, copper, iron, manganese, carbon, silicon, and sulfur. Mechanical requirements including tensile strength, yield strength, and elongation are given for specific conditions and diameter or distance between parallel surfaces. Chemical analysis, tension test, and hardness test shall be performed.


SDO ASTM: ASTM International
Document Number B160
Publication Date May 1, 2005
Language en - English
Page Count 6
Revision Level 05e1
Supercedes
Committee B02.07
Publish Date Document Id Type View
April 1, 2024 B0160-24 Revision
Oct. 1, 2009 B0160-05R09E01 Revision
May 1, 2005 B0160-05E01 Revision
May 1, 2005 B0160-05 Revision
May 10, 1999 B0160-99 Revision
April 1, 2019 B0160-05R19 Reaffirmation
Oct. 1, 2014 B0160-05R14 Reaffirmation
Oct. 1, 2009 B0160-05R09 Reaffirmation