ASTM A852/A852M-03(2007)

Current Revision

Standard Specification for Quenched and Tempered Low-Alloy Structural Steel Plate with 70 ksi [485 MPa] Minimum Yield Strength to 4 in. [100 mm] Thick (Withdrawn 2010)

$73.00

$73.00

$131.40


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

...

1.1 This specification covers quenched and tempered high-strength low-alloy structural steel plates for welded, riveted, or bolted construction. It is intended primarily for use in welded bridges and buildings where savings in weight, added durability, and good notch toughness are important. The atmospheric corrosion resistance of this steel in most environments is substantially better than that of carbon structural steels with or without copper addition (see Note 1). When properly exposed to the atmosphere, this steel can be used bare (unpainted) for many applications. Welding technique is of fundamental importance, and it is presupposed that the welding procedure will be suitable for the steel and the intended service. This specification is limited to material up to 4 in. [100 mm], inclusive, in thickness. See Appendix X3 of Specification A 6/A 6M for information on weldability. Note 1—For methods of estimating the atmospheric corrosion resistance of low-alloy steels, see Guide G 101.

1.2 Plates produced under this specification are impact tested at a temperature not higher than 50°F [10°C].

1.3 The values stated in inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each item are not exact equivalents. Therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.


This specification covers quenched and tempered high-strength low-alloy structural steel plates for welded, riveted, or bolted construction. It is intended primarily for use in welded bridges and buildings where savings in weight, added durability, and good notch toughness are important. When properly exposed to the atmosphere, this steel can be used bare (unpainted) for many applications. The steel shall conform on heat and product analysis to the chemical composition requirements prescribed for carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, copper, and vanadium. Tensile test requirements shall include: yield strength, tensile strength, and elongation. The requirements for manufacturing, heat treatment, and longitudinal Charpy V-notch impact testing are given as well.


SDO ASTM: ASTM International
Document Number A852
Publication Date Sept. 1, 2007
Language en - English
Page Count 3
Revision Level 03(2007)
Supercedes
Committee A01.02
Publish Date Document Id Type View
Sept. 1, 2007 A0852_A0852M-03R07 Revision
April 10, 2003 A0852_A0852M-03 Revision
Sept. 10, 2001 A0852_A0852M-01 Revision
Sept. 10, 2001 A0852_A0852M-00A Revision