ASTM A709/A709M-09

Historical Revision

Standard Specification for Structural Steel for Bridges

$83.00

$83.00

$149.40


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

...

1.1 This specification covers carbon and high-strength low-alloy steel structural shapes, plates, and bars and quenched and tempered alloy steel for structural plates intended for use in bridges. Seven grades are available in four yield strength levels as follows:

Grade U.S. [SI] Yield Strength, ksi [MPa]
36 [250] 36 [250]
50 [345] 50 [345]
50S [345S] 50 [345]
50W [345W] 50 [345]
HPS 50W [HPS 345W] 50 [345]
HPS 70W [HPS 485W] 70 [485]
HPS 100W [HPS 690W] 100 [690]

1.1.1 Grades 36 [250], 50 [345], 50S [345S], and 50W [345W] are also included in Specifications A 36/A 36M, A 572/A 572M, A 992/A 992M, and A 588/A 588M, respectively. When the supplementary requirements of this specification are specified, they exceed the requirements of Specifications A 36/A 36M, A 572/A 572M, A 992/A 992M, and A 588/A 588M.

1.1.2 Grades 50W [345W], HPS 50W [HPS 345W], HPS 70W [HPS 485W], and HPS 100W [HPS 690W] have enhanced atmospheric corrosion resistance (see 13.1.2). Product availability is shown in Table 1.

1.2 Grade HPS 70W [HPS 485W] or HPS 100W [HPS 690W] shall not be substituted for Grades 36 [250], 50 [345], 50S [345S], 50W [345W], or HPS 50W [HPS 345W]. Grade 50W [345W], or HPS 50W [HPS 345W] shall not be substituted for Grades 36 [250], 50 [345] or 50S [345S] without agreement between the purchaser and the supplier.

1.3 When the steel is to be welded, it is presupposed that a welding procedure suitable for the grade of steel and intended use or service will be utilized. See Appendix X3 of Specification A 6/A 6M for information on weldability.

1.4 For structural products to be used as tension components requiring notch toughness testing, standardized requirements are provided in this standard, and they are based upon American Association of State Highway and Transportation Officials (AASHTO) requirements for both fracture critical and non-fracture critical members.

1.5 Supplementary requirements are available but shall apply only if specified in the purchase order.

1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

1.7 For structural products produced from coil and furnished without heat treatment or with stress relieving only, the additional requirements, including additional testing requirements and the reporting of additional test results, of Specification A 6/A 6M apply.

TABLE 1 Tensile and Hardness RequirementsA

Note—Where . . . appears in this table, there is no requirement.

Grade
Plate Thickness,
in. [mm]
Structural Shape Flange
or Leg
Thickness, in. [mm]
Yield Point
or Yield
Strength,B
ksi
[MPa]
Tensile
Strength,
ksi [MPa]
Minimum Elongation, %
Reduc-
tion of
AreaC,D
min, %
Plates and BarsC,E
ShapesE
8 in.
or 200
mm
2 in.
or 50
mm
8 in.
or 200
mm
2 in.
or 50
mm
36 [250]
to 4 [100], incl
to 3 in. [75 mm], incl
36 [250] min
5880 [400550]
20
23
20
21
...

over 3 in. [75 mm]
36 [250] min
58 [400] min
...
..
20
19
...
50 [345]
to 4 [100], incl
all
50 [345] min
65 [450] min
18
21
18
21F
...
50S [345S] G
all 5065
[345450]HI
65 [450]H min ...
... 18
21
...
50W [345W] and
HPS 50W
[HPS 345W]
to 4 [100], incl
all
50 [345] min
70 [485] min
18
21
18
21J
...
HPS 70W
[HPS 485 W]
to 4 [100], incl G 70 [485] minB 85110 [585760] ...
19K ...
...
...
HPS 100W
[HPS 690W]
to 2½ [65], incl
G
100 [690] minB
110130 [760895]
...
18K
...
...
L

A See specimen orientation and preparation subsection in the Tension Tests section of Specification A 6/A 6M.

B Measured at 0.2 % offset or 0.5 % extension under load as described in Section 13 of Test Methods A 370.

C Elongation and reduction of area not required to be determined for floor plates.

D For plates wider than 24 in. [600 mm], the reduction of area requirement, where applicable, is reduced by five percentage points.

E For plates wider than 24 in. [600 mm], the elongation requirement is reduced by two percentage points. See elongation requirement adjustments in the Tension Tests section of Specification A 6/A 6M.

F Elongation in 2 in. or 50 mm: 19 % for shapes with flange thickness over 3 in. [75 mm].

G Not applicable.

H The yield to tensile ratio shall be 0.87 or less for shapes that are tested from the web location; for all other shapes, the requirement is 0.85.

I A maximum yield strength of 70 ksi [480 MPa] is permitted for structural shapes that are required to be tested from the web location.

J For wide flange shapes with flange thickness over 3 in. [75 mm], elongation in 2 in. or 50 mm of 18 % minimum applies.

K If measured on the Fig. 3 (Test Methods A 370) 1½-in. [40mm] wide specimen, the elongation is determined in a 2-in. or 50-mm gage length that includes the fracture and shows the greatest elongation.

L 40 % minimum applies if measured on the Fig 3 (Test Methods A 370) 1 ½-in. [40-mm] wide specimen; 50 % minimum applies if measured on the Fig. 4 (Test Methods A 370) ½-in. [12.5-mm] round specimen.


This specification covers carbon and high-strength low alloy steel structural shapes, plates and bars and quenched and tempered alloy steel for structural plates intended for use in bridges. Heat analysis shall be used to determine the percentage of carbon, manganese, phosphorus, sulfur, silicon, and copper for the required chemical composition. Tension test shall be used to determine the required tensile properties such as tensile strength, yield strength, and elongation. Materials shall undergo: (1) impact test for non-fracture critical and fracture critical members; and (2) Brinell hardness test for Grades 100 and 100W. Atmospheric corrosion resistance shall also be determined.


SDO ASTM: ASTM International
Document Number A709
Publication Date April 1, 2009
Language en - English
Page Count 7
Revision Level 09
Supercedes
Committee A01.02
Publish Date Document Id Type View
Oct. 15, 2024 A0709_A0709M-24 Revision
Nov. 1, 2021 A0709_A0709M-21 Revision
Nov. 15, 2018 A0709_A0709M-18 Revision
Sept. 1, 2017 A0709_A0709M-17E01 Revision
Sept. 1, 2017 A0709_A0709M-17 Revision
May 1, 2016 A0709_A0709M-16A Revision
Feb. 15, 2016 A0709_A0709M-16 Revision
Sept. 1, 2015 A0709_A0709M-15 Revision
Oct. 1, 2013 A0709_A0709M-13A Revision
May 1, 2013 A0709_A0709M-13 Revision
May 1, 2011 A0709_A0709M-11 Revision
Sept. 1, 2010 A0709_A0709M-10 Revision
Oct. 1, 2009 A0709_A0709M-09A Revision
April 1, 2009 A0709_A0709M-09 Revision
Oct. 1, 2008 A0709_A0709M-08 Revision
March 1, 2007 A0709_A0709M-07 Revision
Sept. 1, 2006 A0709_A0709M-06A Revision
March 15, 2006 A0709_A0709M-06 Revision
April 1, 2005 A0709_A0709M-05 Revision
Sept. 1, 2004 A0709_A0709M-04AE01 Revision
Sept. 1, 2004 A0709_A0709M-04A Revision
April 1, 2004 A0709_A0709M-04 Revision
May 10, 2003 A0709_A0709M-03A Revision
April 10, 2003 A0709_A0709M-03 Revision
Oct. 10, 2001 A0709_A0709M-01BE03 Revision
Oct. 10, 2001 A0709_A0709M-01BE01 Revision
Oct. 10, 2001 A0709_A0709M-01B Revision
Oct. 10, 2001 A0709_A0709M-01A Revision
Oct. 10, 2001 A0709_A0709M-01 Revision
Oct. 10, 2001 A0709_A0709M-00A Revision
Oct. 10, 2001 A0709_A0709M-00 Revision
Oct. 10, 2001 A0709_A0709M-01BE02 Reaffirmation