Current Revision

Standard Specification for Stainless Steel Wire

$69.00

$69.00

$124.20

$83.00

$83.00

$149.40



Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

...

1.1 This specification covers stainless steel wire, except the free-machining types. It includes round, square, octagon, hexagon, and shape wire in coils only for the more commonly used types of stainless steels for general corrosion resistance and high-temperature service. For bars in straightened and cut lengths, see Specifications A276 or A479/A479M.

Note 1: For free-machining stainless wire, designed especially for optimum machinability, see Specification A581/A581M.

1.2 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.

1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.


This specification covers stainless steel wire, except the free-machining types. It includes round, square, octagon, hexagon, and shape wire in coils only for the more commonly used types of stainless steels for general corrosion resistance and high-temperature service. The steel specimens shall undergo the following conditions: (1) annealed as a final heat treatment; (2) cold worked to higher strength; (3) heat treated to an intermediate temper; or (4) heat treated to a hard temper by austenitizing, quenching, and tempering at a relatively low temperature. The materials shall be cold drawn, annealed, and pickled. The steel wires shall conform to the required chemical compositions of carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, molybdenum, nitrogen, and other elements such as niobium , vanadium, copper, tantalum, titanium and cobalt. Mechanical test shall be performed wherein in the steel specimens shall conform to the required values of tensile strength, yield strength, and elongation. The martensitic grades shall conform to the required values of hardness after heat treatment.


SDO ASTM: ASTM International
Document Number A580
Publication Date May 15, 2023
Language en - English
Page Count 5
Revision Level 23
Supercedes
Committee A01.17
Publish Date Document Id Type View
May 15, 2023 A0580_A0580M-23 Revision
March 1, 2018 A0580_A0580M-18 Revision
Sept. 1, 2016 A0580_A0580M-16 Revision
May 1, 2015 A0580_A0580M-15 Revision
Oct. 1, 2014 A0580_A0580M-14 Revision
Oct. 1, 2013 A0580_A0580M-13B Revision
May 1, 2013 A0580_A0580M-13A Revision
April 1, 2013 A0580_A0580M-13 Revision
May 1, 2012 A0580_A0580M-12A Revision
March 1, 2012 A0580_A0580M-12E01 Revision
March 1, 2012 A0580_A0580M-12 Revision
Oct. 1, 2008 A0580_A0580M-08 Revision
March 1, 2006 A0580_A0580M-06 Revision
June 10, 1998 A0580_A0580M-98 Revision
Sept. 1, 2004 A0580_A0580M-98R04 Reaffirmation