ASTM A414/A414M-07

Historical Revision

Standard Specification for Steel, Sheet, Carbon, and High-Strength, Low-Alloy for Pressure Vessels

$73.00

$73.00

$131.40


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

...

1.1 This specification covers hot-rolled carbon steel sheet for pressure vessels involving fusion welding or brazing. Welding and brazing technique is of fundamental importance and shall be in accordance with commercial practices.

1.2 The following grades are included in this specification:

Mechanical Requirements
GradeYield Strength, minTensile Strength, min
ksiMPa ksiMPa
A2517045310
B3020550345
C3323055380
D3524060415
E3826065450
F4229070485
G4531075515

1.3 Hot-rolled carbon steel sheet is generally furnished in cut lengths and to decimal thickness only. Coils may be furnished, provided tension test specimens are taken to represent the middle of the slab as required by 5.1.4. The purchaser should recognize this may require cutting the coils to obtain test samples and results in half-size coils. The sheet is furnished to the following size limits:

Width, in. [mm]
Thickness, in. [mm]Over 12 [Over 300]
0.270 to 0.230 [7.0 to 6.0]sheet (coils only)
Under 0.230 to 0.057 [6.0 to 1.5] sheet

1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

1.5 Tolerances are found in General Requirements Specifications A 568/A 568M and A 635/A 635M. The appropriate General Requirements specification is applied based on the thickness and width of the product ordered.


This specification covers hot-rolled carbon steel sheet for pressure vessels involving fusion welding or brazing. Tensile and yield strengths shall be determined after a tension test of the sheets. The material shall be furnished without removing the hot-rolled oxide or scale. When required, the material may be specified to be pickled or blast cleaned. When specified to be pickled or blast cleaned, the material shall be furnished oiled. When required, pickled or blast-cleaned material may be specified to be furnished dry.


SDO ASTM: ASTM International
Document Number A414
Publication Date May 15, 2007
Language en - English
Page Count 4
Revision Level 07
Supercedes
Committee A01.19
Publish Date Document Id Type View
Aug. 15, 2024 A0414_A0414M-24 Revision
Nov. 1, 2023 A0414_A0414M-23 Revision
May 1, 2014 A0414_A0414M-14 Revision
May 1, 2013 A0414_A0414M-13 Revision
April 1, 2010 A0414_A0414M-10 Revision
Nov. 1, 2009 A0414_A0414M-09 Revision
May 15, 2007 A0414_A0414M-07 Revision
March 1, 2006 A0414_A0414M-06 Revision
March 1, 2005 A0414_A0414M-05 Revision
March 1, 2004 A0414_A0414M-04 Revision
Sept. 10, 2001 A0414_A0414M-01 Revision
Sept. 10, 2001 A0414_A0414M-00 Revision
Sept. 1, 2019 A0414_A0414M-14R19 Reaffirmation