ASTM A278/A278M-01(2006)

Historical Reaffirmation

Standard Specification for Gray Iron Castings for Pressure-Containing Parts for Temperatures Up to 650 °F (350 °C)

$73.00

$73.00

$131.40


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


...

1.1 This specification covers gray iron for castings suitable for pressure-containing parts for use at temperatures up to 650°F (350°C).

1.2 Classes of Iron:

1.2.1 Castings of all classes are suitable for use up to 450°F (230°C). For temperatures above 450°F and up to 650°F, only Class 40, 45, 50, 55, and 60 castings are suitable.

1.2.2 Castings of all clases are suitable for use up to 230°C. For temperatures above 230°C and up to 350°C, only Class 275, 300, 325, 350, 380, and 415 castings are suitable.


This specification covers gray iron for castings suitable for pressure-containing parts at elevated temperatures. Castings shall be stress-relieved by placing them in a suitable furnace and heating them uniformly to the temperatures and for the times specified. Castings to be used at a particular temperature range shall undergo heat treatment and cooling. Chemical analysis shall be performed on each class of castings and shall meet the maximum requirement for carbon, phosphorus and sulfur. Iron used in supplying castings shall conform to the required tensile strength. Separately cast test bars having the required dimensions shall be poured from the same lot as the castings represented. The test bars shall be cast in dried siliceous sand molds maintained at approximately room temperature. Tension test shall be performed on each lot and materials shall conform to the tensile requirements specified.


SDO ASTM: ASTM International
Document Number A278
Publication Date Oct. 1, 2006
Language en - English
Page Count 4
Revision Level 01(2006)
Supercedes
Committee A04.01
Publish Date Document Id Type View
June 10, 2001 A0278_A0278M-01 Revision
Oct. 1, 2024 A0278_A0278M-01R24 Reaffirmation
May 1, 2020 A0278_A0278M-01R20 Reaffirmation
Nov. 1, 2015 A0278_A0278M-01R15 Reaffirmation
March 1, 2011 A0278_A0278M-01R11 Reaffirmation
Oct. 1, 2006 A0278_A0278M-01R06 Reaffirmation