Logo

ASTM A276-13a

Current Revision

Standard Specification for Stainless Steel Bars and Shapes

$83.00

$83.00

$149.40

$0.00

$0.00

$0.00



Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

...

1.1 This specification covers hot-finished or cold-finished bars except bars for reforging (Note 1). It includes rounds, squares, and hexagons, and hot-rolled or extruded shapes, such as angles, tees, and channels in the more commonly used types of stainless steels. The free-machining types (Note 2) for general corrosion resistance and high-temperature service are covered in a separate specification.

Note 1For bars for reforging, see Specification A314.
Note 2For free-machining stainless bars designed especially for optimum machinability, see Specification A582/A582M.
Note 3There are standards covering high nickel, chromium, austenitic corrosion, and heat resisting alloy materials. These standards are under the jurisdiction of ASTM Subcommittee B02.07 and may be found in Annual Book of ASTM Standards, Vol. 02.04.

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.


This specification covers hot-finished or cold-finished bars except bars for reforging. It includes rounds, squares, and hexagons, and hot-rolled or extruded shapes, such as angles, tees, and channels in the more commonly used types of stainless steels. The bars shall be furnished in one of the following conditions: Condition A in which the bars are annealed, Condition H in which the bars are hardened and tempered at a relative temperature, Condition T in which the bars are hardened and tempered at a relatively high temperature, Condition S in which the bars are strain hardened or relatively light cold worked, and Condition B in which the bars are relatively severe cold worked. The material shall be subjected to a mechanical test to determine its tensile strength, yield strength, elongation, and Brinell hardness.


SDO ASTM: ASTM International
Document Number A276
Publication Date Nov. 1, 2013
Language en - English
Page Count 8
Revision Level 13a
Supercedes
Committee A01.17
Publish Date Document Id Type View
Nov. 1, 2013 A0276-13A Revision
May 1, 2013 A0276-13 Revision
May 1, 2010 A0276-10 Revision
Oct. 1, 2008 A0276-08A Revision
May 15, 2008 A0276-08 Revision
March 1, 2006 A0276-06 Revision
Sept. 1, 2005 A0276-05A Revision
March 1, 2005 A0276-05 Revision
Feb. 1, 2004 A0276-04 Revision
April 10, 2003 A0276-03 Revision
Sept. 10, 2002 A0276-02A Revision
March 10, 2002 A0276-02 Revision
March 10, 2002 A0276-00AE01 Revision
March 10, 2002 A0276-00A Revision
Not Available A0276-98B Revision