ASTM A1106/A1106M-17(2024)

Historical Reaffirmation

Standard Specification for Pressure Vessel Plate, Alloy Steel, Austenitic High Manganese for Cryogenic Application

$61.00

$61.00

$109.80


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


Stay effortlessly up-to-date with the latest standard revisions. When new versions are released, they're automatically charged and delivered to you, ensuring seamless compliance.

Document Preview Not Available...

1.1 This specification2 covers austenitic high-manganese alloy steel plates produced by hot rolling and controlled cooling. The plates are intended primarily for use in welded pressure vessels.

1.2 Due to the inherent characteristics of the rolling and cooling processes, or both, the plates shall not be formed at temperatures exceeding 932 °F [500 °C].

1.3 The maximum thickness of plates is limited only by the capacity of the material to meet the specified mechanical property requirements; however, current mill practice normally limits this material to 2.5 in. [63.5 mm] max.

1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.


This specification covers the general requirements, manufacturing practice, and corresponding test methods for austenitic high-manganese alloy steel plates produced by hot rolling and controlled cooling and intended primarily for use in welded pressure vessels. Due to the inherent characteristics of the rolling and cooling processes, or both, the plates shall not be formed at temperatures exceeding 932°F [500°C]. The maximum thickness of plates is limited only by the capacity of the material to meet the specified mechanical property requirements; however, current mill practice typically limits this material to 2.5 in. [63.5 mm] max.


SDO ASTM: ASTM International
Document Number A1106
Publication Date Aug. 15, 2024
Language en - English
Page Count 3
Revision Level 17(2024)
Supercedes
Committee A01.11
Publish Date Document Id Type View
March 15, 2017 A1106_A1106M-17 Revision
Aug. 15, 2024 A1106_A1106M-17R24 Reaffirmation